摘要:试验了Incoloy825合金电极(/%:0.01C,0.21Si,0.41Mn,0.007S,0.019P,22.33Cr,39.08Ni,3.04Mo,2.14Cu,1.17Ti,0.17A1)由3t中频炉+3t AOD冶炼,并经抽锭电渣重熔成280mm×325 mm坯(/%:0.01C,0.210.23Si,0.40Mn,0.005S,0.0230.024P,22.4822.50Cr,39.1039.13Ni,3.053.07Mo,2.142.15Cu,1.001.10Ti,0.150.18Al)。试验表明,Incoloy825合金方坯抽锭电渣重熔过程中,由于Ti烧损,渣中TiO2含量不断增加,熔渣的粘度也不断上升,导致钢渣不易分离。通过改进抽锭电渣重熔渣系配比,采用(/%)57CaF2,15CaO,5MgO,15Al2O3,5SiO2,3TiO2渣系以及控制电极熔化速度680kg/h,重熔过程加0.43kg/t铝粒以控制Ti烧损,使Incoloy825合金铸坯表面质量明显改善。
注:因版权方要求,不能公开全文,如需全文,请咨询杂志社
热门期刊服务
China Ocean Engineering Journal of Bionic Engineering Earthquake Engineering and Engineering Vibration Chinese Journal of Mechanical Engineering Water Science and Engineering Frontiers of Information Technology Electronic Engineering Chinese Journal of Chemical Engineering International Journal of Computing Journal of Integrative Agriculture Journal of Systems Engineering and Electronics International Journal of Oral Science Journal of Beijing Institute of Technology